Top Level > Clear Heatshrink 2:1 Ratio
19.1mm Diameter Clear Heatshrink
£2.04
Clear Heatshrink 19.1mm Diameter x 1m
Supplied in 1 metre lengths
Shrink ratio 2:1
Shrinking temperature +80ºc
Made from polyolefin
Excellent flexibility and insulation
Excellent flame retardent properties
Temperature range -55°c to +125°c
UL approved
19.1mm is the internal diameter before shrinking
Purchase more than 1 length and it will be supplied in one continuous length
Weight per 1m length: 34grms
Heatshrink Measurements:
D = Diameter
F= Lay Flat Measurement
|
Inner Diameter mm |
Wall Thickness As Supplied mm |
Wall Thickness After Recovery mm |
|
1.0mm |
0.15 +/- 0.05 |
0.22 +/- 0.10 |
|
1.6mm |
0.15 +/- 0.05 |
0.28 +/- 0.10 |
|
2.4mm |
0.18 +/- 0.05 |
0.35 +/- 0.10 |
|
3.2mm |
0.18 +/- 0.05 |
0.40 +/- 0.10 |
|
4.8mm |
0.25 +/- 0.05 |
0.50 +/- 0.10 |
|
6.4mm |
0.28 +/- 0.05 |
0.55 +/- 0.10 |
|
9.5mm |
0.30 +/- 0.08 |
0.60 +/- 0.10 |
|
12.7mm |
0.30 +/- 0.08 |
0.60 +/- 0.10 |
|
19.1mm |
0.40 +/- 0.15 |
0.80 +/- 0.15 |
|
25.4mm |
0.55 +/- 0.15 |
0.90 +/- 0.15 |
|
38.1mm |
0.55 +/- 0.15 |
1.00 +/- 0.15 |
|
50.8mm |
0.60 +/- 0.18 |
1.00 +/- 0.15 |
|
76mm |
0.70 +/- 0.20 |
1.46 +/- 0.20 |
|
102mm |
0.70 +/- 0.20 |
1.46 +/- 0.20 |
|
127mm |
0.70 +/- 0.20 |
1.56 +/- 0.25 |
|
152mm |
0.80 +/- 0.25 |
1.66 +/- 0.25 |
|
178mm |
0.80 +/- 0.25 |
1.66 +/- 0.25 |
Technical Data
Property
Test Method
Typical Data
Tensile Strength
ASTM D 2671
14MPa
Ultimate Elongation (%)
ASTM D 2671
450
Longitudinal Shrinkage (%)
UL 224
+/- 5
Heat Aging
Tensile Strength
Ultimate Elongation (%)
158¡É,
168hr
11MPa
300
Flammability
UL224 VW-1
Pass
Heat shock (250¡É,
4hrs)
ASTM D 2671
No cracking
Cold bend tests (-55¡É,
4hrs)
ASTM D 2671
No cracking
Dielectric Strength (kv/mm)
ASTM D 150
20
Volume Resistivity (ohm-cm)
ASTM D 876
1x1014
Copper Stability
UL224
Pass